Two methods to reduce the hardness of liquid silicone
Source:
|
Author:SENLEEMOLD
|
Published time: 2020-11-17
|
478 Views
|
Share:
The hardness of liquid silicone is generally adjusted according to the needs of the application, but some users find that the hardness of the silicone mold made is too high. This happens to new users with inexperience, so if you encounter this problem, how to solve it Well, the following Senli silicone mold products manufacturers provide two methods to reduce the hardness. Experienced liquid silica gel users will know that the actual silica gel hardness and the data you provide to the manufacturer have a certain error range. This error is generally about ±2 Shore A. Especially for novices who are uncertain about the hardness they need, this will cause greater hardness errors.
液体硅胶的硬度一般是根据用途需求来调节的,但有些用户发现做出来的硅胶模具硬度偏高,这种情况多发生在没经验的新用户身上,那么如果遇到了这种问题,该如何解决呢,下面森力硅胶模具制品厂家提供两种能降低硬度的方法。
有经验的液体硅胶用户都会知道买来的硅胶,实际硅胶硬度和你给厂家提供的数据是有一定的误差范围的,这种误差一般在±2邵氏A左右。特别是对于新手对自己需要的硬度不确定,这样会造成更大的硬度误差。
第一种方法:我们可以使用硅油来降低硅胶硬度,一般加入1%的硅油,硅胶硬度会降低0.9~1.1度左右;加入10%的硅油,硅胶硬度会降低5度左右。但在实际操作中如果添加的硅油比列过大会破坏硅胶的分子量,抗撕、抗拉强度都会相应的变差,从而影响硅胶模具的使用寿命,另外硅油添加比例太大也会导致硅橡胶模具容易变形。所以,我们建议:一般硅胶与硅油的比例不超过5%,并且尽量加粘度较大些的硅油,如果加入超过5%的硅油,请先小量试用确定做出来的模具能否使用。
第二种方法:采用高硬度硅胶和低硬度硅胶混合,使用这种方法前提是你购买了两种硬度的硅胶,比如20硬度的硅胶和10硬度的硅胶混合后硅胶的硬度在15邵氏A左右。使用这种混合的方法应注意,缩合型的不能和加成型的混合使用,否则会造成不固化的现象(加成型模具硅胶与缩合型模具硅胶的区别)。